廠家(產(chǎn)地) | 美國杜邦 |
---|---|
牌號 | 158L NC010 |
加工級別 | 注塑級 |
特性級別 | 耐磨 |
銷售方式 | 品牌經(jīng)銷 |
類型 | 標(biāo)準(zhǔn)料 |
注塑級 | 耐磨 |
性能項(xiàng)目 | 測試條件 | 測試方法 | 數(shù)值/描述 | 單位 | |
機(jī)械性能 | 拉伸強(qiáng)度(引張強(qiáng)度) | ASTM D638/ISO 527 | 83 | kg/cm²(MPa)[Lb/in2] | |
斷裂伸長率 | ASTM D638/ISO 527 | 50 | % | ||
拉伸模量 | ASTM D638/ISO 527 | kg/cm²(MPa)[Lb/in2] | |||
拉伸屈服伸長率(延伸率) | ASTM D638/ISO 527 | 4 | % | ||
拉伸斷裂伸長率(延伸率) | ASTM D638/ISO 527 | 83 | % | ||
彎曲模量(彎曲彈性率) | ASTM D790/ISO 178 | 2800 | kg·cm/cm(J/M)ft·lb/in | ||
彎曲強(qiáng)度 | ASTM D790/ISO 178 | kg·cm/cm(J/M)ft·lb/in | |||
洛氏硬度 | ASTM D785 | ||||
IZOD 缺口沖擊強(qiáng)度 | 1/4" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
1/4" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
1/8" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
1/8" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
Charpy沖擊強(qiáng)度 | 23℃ (缺口) | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
-30℃(缺口) | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
23℃(無缺口) | ASTM D256/ISO 179 | 53 | kg·cm/cm(J/M)ft·lb/in | ||
-30℃(無缺口) | ASTM D256/ISO 179 | 105 | kg·cm/cm(J/M)ft·lb/in | ||
物性性能 | 比重(密度) | ASTM D792/ISO 1183 | 1.14 | ||
成型收縮率 | ASTM D955 | % | |||
熔融指數(shù)(流動系數(shù)) | 200℃/5kg | ASTM D1238/ISO 1133 | g/10min | ||
220℃/10kg | ASTM D1238/ISO 1133 | g/10min | |||
吸水率 23℃/24H | ASTM D570/ISO 62 | 1.2 | % | ||
熱性能 | 熱變形溫度 | 退火 | ASTM D648/ISO 75 | 210 | ℃(℉) |
未退火 | ASTM D648/ISO 75 | 65 | ℃(℉) | ||
維卡軟化點(diǎn) | ASTM D1525/ISO R306 | ℃(℉) | |||
熔點(diǎn) | - | 262 | ℃(℉) | ||
燃燒性(率) | UL94 | 0.71 | |||
線性膨脹系數(shù) | ASTM D696/ISO 11359 | 16.5 | mm/mm.℃ | ||
電氣性能 | 介電常數(shù) | 100HZ | ASTM D150/IEC 60250 | 23.2 | |
1MHZ | ASTM D150/IEC 60250 | 4.0 | |||
體積電阻率 | ASTM D257/IEC 60093 | 1015 | Ω.cm | ||
表面電阻率 | ASTM D257/IEC 60093 | 1014 | Ω | ||
耐電弧性 | ASTM D495/IEC 60112 | ||||
加工條件 | 干燥條件 | ||||
加工溫度 | 射嘴 | ℃ | |||
料筒前段 | ℃ | ||||
料筒中段 | ℃ | ||||
料筒后段 | ℃ | ||||
熔體溫度 | ℃ | ||||
模具溫度 | ℃ | ||||
壓力 | 注塑壓力 | Mpa | |||
保壓壓力 | Mpa | ||||
背壓 | Mpa | ||||
螺桿轉(zhuǎn)速 | rpm |