牌號(hào) | 進(jìn)口 |
---|---|
廠家 | 進(jìn)口 |
用途級(jí)別 | 擠出、注塑 |
品牌 | 擠出級(jí)tpu新料 |
型號(hào) | 85a-95a |
95A性能參數(shù)
性 能Property | 測(cè)試條件Test Condition | 單位Unit | 測(cè)試標(biāo)準(zhǔn)Standard | 結(jié) 果Result | |
硬度hardness | Shore A | 23℃/50% | Shore A | ISO R868A | 95 |
Shore D | 23℃/50% | Shore D | ISO R868D | 51 | |
色度Color | 23℃/50% | APHA | Inter- Standard | 31 | |
密度Specific Gravity | 23℃/50% | g/cm3 | ISO 1183 | 1.22 | |
50% 模量50% Modulus | 23℃/50% | MPa | ISO 37 | 15 | |
100% 模量100% Modulus | 23℃/50% | MPa | ISO 37 | 20 | |
300%模量300% Modulus | 23℃/50% | MPa | ISO 37 | 30 | |
拉伸斷裂強(qiáng)度Tensile broken strength | 23℃/50% | MPa | ISO37:1994(E) | 35 | |
斷裂伸長(zhǎng)率Ultimate Elongation | 23℃/50% | % | ISO37:1994(E) | 450 | |
撕裂強(qiáng)度Tear strength | 23℃/50% | KN/M | ISO34-1:2004(E) | 180 | |
熔融指數(shù)Melting index | 23℃/50% | g/10min | Inter- Standard | 40 | |
磨 耗Abrasion Loss | 23℃/50% | mg | ASTM D3489 | / | |
維卡軟化溫度Vicat Softening Temperature | 23℃/50% | ℃ | ASTM D1525 | 116 |
性 能Property | 測(cè)試條件Test Condition | 單位Unit | 測(cè)試標(biāo)準(zhǔn)Standard | 結(jié) 果Result | |
硬度hardness | Shore A | 23℃/50% | Shore A | ISO R868A | 85A |
Shore D | 23℃/50% | Shore D | ISO R868D | ||
色度Color | 23℃/50% | APHA | Inter- Standard | ||
密度Specific Gravity | 23℃/50% | g/cm3 | ISO 1183 | 1.19 | |
50% 模量50% Modulus | 23℃/50% | MPa | ISO 37 | 4.5 | |
100% 模量100% Modulus | 23℃/50% | MPa | ISO 37 | 6 | |
300%模量300% Modulus | 23℃/50% | MPa | ISO 37 | 11 | |
拉伸斷裂強(qiáng)度Tensile broken strength | 23℃/50% | MPa | ISO37:1994(E) | 40 | |
斷裂伸長(zhǎng)率Ultimate Elongation | 23℃/50% | % | ISO37:1994(E) | 530 | |
撕裂強(qiáng)度Tear strength | 23℃/50% | KN/M | ISO34-1:2004(E) | 130 | |
熔融指數(shù)Melting index | 23℃/50% | g/10min | Inter- Standard | 19 | |
磨 耗Abrasion Loss | 23℃/50% | mg | ASTM D3489 | 45 | |
維卡軟化溫度Vicat Softening Temperature | 23℃/50% | ℃ | ASTM D1525 | 85 |