產(chǎn)品參數(shù)
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 |
吸水量 | 24小時浸漬 | ASTM D-570 | 0.31 | % |
吸水量 | 50%相對濕度 | ASTM D-570 | 0.27 | % |
比重 | 聽 | ASTM D-792 | 1.39 | |
吸水量 | 浸漬平衡點 | ASTM D-570 | 0.75 | % |
模收縮 | 聽 | 聽 | 1.7-1.9 | % |
撓曲變形強(qiáng)度 | 23℃ | ASTM D-790 | 70 | MPa |
洛氏硬度 | 聽 | ASTM D-785 | 117 | R scale |
線性熱膨脹系數(shù) | 60~104℃ | ASTM D-696 | 12.4 | 10-5m/m℃ |
拉伸強(qiáng)度 | 122℃ | ASTM D-638 | >16 | MPa |
撓曲系數(shù) | 100℃ | ASTM D-790 | 690 | MPa |
撓曲系數(shù) | 23℃ | ASTM D-790 | 2420 | MPa |
撓曲系數(shù) | 70℃ | ASTM D-790 | 1260 | MPa |
抗剪強(qiáng)度 | 23℃ | ASTM D-732 | 49 | MPa |
IZOD沖擊試驗 | 缺口-40℃ | ASTM D-256 | 106 | j/m |
破裂點拉伸變形量 | 122℃ | ASTM D-638 | >505 | % |
破裂點拉伸變形量 | -55℃ | ASTM D-638 | 22 | % |
拉伸強(qiáng)度 | 70℃ | ASTM D-638 | >38 | MPa |
負(fù)載變形量 | 140kg/cm250℃ | ASTM D-621 | 0.9 | % |
拉伸強(qiáng)度 | -55℃ | ASTM D-638 | 99 | MPa |
撓曲系數(shù) | -55℃ | ASTM D-790 | 3670 | MPa |
拉伸強(qiáng)度 | 100℃ | ASTM D-638 | >23 | MPa |
壓縮應(yīng)力 | 23℃ 1%變形 | ASTM D-695 | 16 | MPa |
抗拉伸沖擊強(qiáng)度 | 長試片23℃ | ASTM D-1822 | 835 | kj/m2 |
破裂點拉伸變形量 | 23℃ | ASTM D-638 | 91 | % |
撓曲疲勞忍耐限度 | 50%RH 23℃ 106周期 | ASTM D-671 | 25 | MPa |
彈性系數(shù) | 23℃ | ASTM D-638 | 2330 | MPa |
IZOD沖擊試驗 | 23℃ | ASTM D-256 | 143 | j/m |
破裂點拉伸變形量 | 100℃ | ASTM D-638 | >585 | % |
撓曲系數(shù) | 122℃ | ASTM D-790 | 420 | MPa |
洛氏硬度 | 聽 | ASTM D-785 | 79 | M scale |
破裂點拉伸變形量 | 70℃ | ASTM D-638 | >545 | % |
壓縮應(yīng)力 | 23℃ 10%變形 | ASTM D-695 | 82 | MPa |
拉伸強(qiáng)度 | 23℃ | ASTM D-638 | 58 | MPa |
容積電阻率 | 23℃ 0.2%含水量 | ASTM D-257 | 2.3×1015 | Ω.cm |
介電因數(shù) | 50%RH 23℃ 106Hz | ASTM D-150 | 0.016 | |
介電常數(shù) | 50%RH 23℃ 102~106Hz | ASTM D-150 | 3.6 | ohm-cm |
抗電弧 | 3.1mm | ASTM D-495 | 120 | sec |
介電強(qiáng)度 | 瞬間Short time(2.3mm) | ASTM D-149 | 15.1(2.3) | kv/mm |
熔點 | ASTM D-2133 | 聽 | 175 | ℃ |
自燃性 | 聽 | UL-94 | HB | |
熱畸變溫度 | 1.8MPa | ASTM D-648 | 85 | ℃ |
線性熱膨脹系數(shù) | 104~160℃ | ASTM D-696 | 15.7 | 10-5m/m℃ |
線性熱膨脹系數(shù) | 29~60℃ | ASTM D-696 | 12.0 | 10-5m/m℃ |
熱畸變溫度 | 0.5MPa | ASTM D-648 | 174 | ℃ |
線性熱膨脹系數(shù) | -40~29℃ | ASTM D-696 | 10.2 | 10-5m/m℃ |