性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
物理性能 | 比重 | ASTM D-792 | 1.51 | ||
吸收率 | 23℃ 60%RH | ASTM D-570 | 0.18 | % | |
熔體流動速率 | ASTM D-1238 | 5 | g/10min | ||
伸長率 | 23℃ | ASTM D-638 | 15 | % | |
成型收縮率 | t3mm 直徑100mm | 2.1 | % | ||
機械性能 | 拉伸沖擊強度 | t3.2mm Stype | ASTM D-1822 | 40 | kgf.cm/cm2 |
拉伸強度 | 23℃ | ASTM D-638 | 440 | kgf/cm2 | |
斷裂強度 | t2mm | ASTM D-732 | 421 | kgf/cm2 | |
Izod缺口沖擊強度 | Notch t3.2mm | ASTM D-256 | 4.0 | kgf.cm/cm | |
洛氏硬度 | ASTM D-785 | 70 | M | ||
彎曲彈性率 | 23℃ | ASTM D-790 | 2.00×104 | kgf/cm2 | |
彎曲強度 | 23℃ | ASTM D-790 | 650 | kgf/cm2 | |
電氣性能 | 耐電壓 | ASTM D-149 | 16 | KV/mm | |
導電率 | 106Hz | ASTM D-150 | 3.1 | ||
體積電阻率 | ASTM D-257 | 1×1014 | Ω.cm | ||
個質(zhì)損耗系數(shù) | 106Hz | ASTM D-150 | 0.009 | ||
表面電阻率 | ASTM D-257 | 1×1016 | Ω | ||
熱性能 | 熱變形溫度 | 4.6kgf/cm2 | ASTM D-648 | 156 | ℃ |
熔點 | 10℃/min | DSC Method | 165 | ℃ | |
熱變形溫度 | 18.6kgf/cm2 | ASTM D-648 | 106 | ℃ | |
線性膨脹系數(shù) | 20℃ -80℃ | ASTM D-696 | 13×10-5 | mm/mm/℃ | |
阻燃性 | t0.8mm | UL-94 | HB |