LG ABS AF312C 物性表
基本信息
黃卡編號 | |
特性 |
|
用途 |
|
加工方法 |
|
比重 | 1.18 | g/cm³ | ASTM D792 |
熔流率(熔體流動速率) (220°C/10.0 kg) | 58 | g/10 min | ASTM D1238 |
收縮率 - 流動 (3.20 mm) | 0.40 到 0.70 | % | ASTM D955 |
洛氏硬度 (R 級) | 104 | ASTM D785 |
拉伸模量 1(3.20 mm) | 2160 | MPa | ASTM D638 |
抗張強度 2(屈服, 3.20 mm) | 45.1 | MPa | ASTM D638 |
伸長率 3 | ASTM D638 | ||
屈服, 3.20 mm | 5.0 | % | ASTM D638 |
斷裂, 3.20 mm | 20 | % | ASTM D638 |
彎曲模量 4(6.40 mm) | 2550 | MPa | ASTM D790 |
彎曲強度 5(屈服, 6.40 mm) | 68.6 | MPa | ASTM D790 |
懸壁梁缺口沖擊強度 | ASTM D256 | ||
-30°C, 3.20 mm | 78 | J/m | ASTM D256 |
-30°C, 6.40 mm | 78 | J/m | ASTM D256 |
23°C, 3.20 mm | 260 | J/m | ASTM D256 |
23°C, 6.40 mm | 230 | J/m | ASTM D256 |
載荷下熱變形溫度 | ASTM D648 | ||
0.45 MPa, 未退火, 6.40 mm 6 | 84.0 | °C | ASTM D648 |
0.45 MPa, 未退火, 6.40 mm 7 | 76.0 | °C | ASTM D648 |
維卡軟化溫度 | 84.0 | °C | ASTM D1525 8 |
RTI Elec | 80.0 | °C | UL 746 |
RTI Imp | 70.0 | °C | UL 746 |
RTI | 80.0 | °C | UL 746 |
UL 阻燃等級 | UL 94 | ||
2.50 mm | V-0 | UL 94 | |
3.00 mm | V-0 | UL 94 |
干燥溫度 | 70.0 到 80.0 | °C | |
干燥時間 | 2.0 到 4.0 | hr | |
建議的最大水分含量 | < 0.010 | % | |
料筒后部溫度 | 170 到 190 | °C | |
料筒中部溫度 | 180 到 200 | °C | |
料筒前部溫度 | 190 到 210 | °C | |
射嘴溫度 | 200 到 230 | °C | |
加工(熔體)溫度 | 200 到 230 | °C | |
模具溫度 | 40.0 到 60.0 | °C | |
背壓 | 0.490 到 0.981 | MPa | |
螺桿轉(zhuǎn)速 | 30 到 60 | rpm |
1 . | 1.0 mm/min |
2 . | 50 mm/min |
3 . | 50 mm/min |
4 . | 15 mm/min |
5 . | 15 mm/min |
6 . | 4.6kg |
7 . | 18.6kg |
8 . | 速率 A (50°C/h), 載荷2 (50N) |